Properties of GG NFRPP Print

Property Table of GGF022J *


Properties
性能
Test Method
方法
Test Condition
条件
GGF022J Unit
单位
Melt Flow Rate
熔体质量流动速率
ISO 1133/ASTM
D1238/GB3682-83
200°C, 10 kg 6 g/10min
230°C, 2.16 kg 1
Density
密度
ISO 1183/ASTM
D792/GB3682-83
1.33 g/cm3
Tensile Strength
拉伸强度
ISO 527/ASTM
D638/GB1040-79
23°C, 50% 56 MPa
Tensile Modulus
拉伸模量
5,100
Tensile Elongation
拉伸长度
2.9 %
Flexural Strength
弯曲强度
ISO 178/ASTM
D790/GB9341-88
23°C, 50% 81 MPa
Flexural Modulus
弯曲模量
4,600
Flexural Elongation
弯曲延伸率
3.6 %
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 23°C, 50% 22 kJ/m2
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 3.5 kJ/m2
Heat Deflection Temperature
热变形温度
ISO 75 /
ASTM D648
0.45 MPa 151 °C
1.82 MPa 129
Shrinkage
收缩率
0.2 – 0.5 %
Flammability UL94
阻燃性
IEC60695-11-10 4mm 5VB
2.5mm V0
1.5mm

V0


Property Table of GGN023J *

Properties
性能
Test Method
方法
Test Condition
条件
GGF022J Unit
单位
Melt Flow Rate
熔体质量流动速率
ISO 1133/ASTM
D1238/GB3682-83
200°C, 10 kg 7
g/10min
230°C, 2.16 kg 2
Density
密度
ISO 1183/ASTM
D792/GB3682-83

1.04 g/cm3
Tensile Strength
拉伸强度
ISO 527/ASTM
D638/GB1040-79
23°C, 50% 56
MPa
Tensile Modulus
拉伸模量
4,100
Tensile Elongation
拉伸长度
3.8 %
Flexural Strength
弯曲强度
ISO 178/ASTM
D790/GB9341-88
23°C, 50% 79
MPa
Flexural Modulus
弯曲模量
3,300
Flexural Elongation
弯曲延伸率
4.5 %
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 23°C, 50% 22
kJ/m2
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 4
kJ/m2
Heat Deflection Temperature
热变形温度
ISO 75 /
ASTM D648
0.45 MPa 151 °C
1.82 MPa 97
Shrinkage
收缩率


0.2 – 0.5 %

Property Table of GGN026J *

Properties
性能
Test Method
方法
Test Condition
条件
GGF022J Unit
单位
Melt Flow Rate
熔体质量流动速率
ISO 1133/ASTM
D1238/GB3682-83
200°C, 10 kg 5
g/10min
230°C, 2.16 kg 1
Density
密度
ISO 1183/ASTM
D792/GB3682-83

1.11 g/cm3
Tensile Strength
拉伸强度
ISO 527/ASTM
D638/GB1040-79
23°C, 50% 62
MPa
Tensile Modulus
拉伸模量
5,400
Tensile Elongation
拉伸长度
2.3 %
Flexural Strength
弯曲强度
ISO 178/ASTM
D790/GB9341-88
23°C, 50% 89
MPa
Flexural Modulus
弯曲模量
4,900
Flexural Elongation
弯曲延伸率
2.9 %
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 23°C, 50% 2122
kJ/m2
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 4
kJ/m2
Heat Deflection Temperature
热变形温度
ISO 75 /
ASTM D648
0.45 MPa 156 °C
1.82 MPa 134
Shrinkage
收缩率


0.2 – 0.5 %

* The above values are obtained by testing under standard room temperature. These values are only for reference and not definitive. Changes in working condition may result in end product characteristics which may deviate from above.


OTHER PROPERTIES of GG NFR PP

fig15

 

  Flame Test

  •    Test according to UL94
  •    GG NF50PP: 50% Nature Fiber (Flex)
  •    Flame Retardant: Halogen, aluminum, Magnesium free
  •   


Rheology: Rosand Capillary Rheometer

fig28


Machine Residence Time: Hot Melting Injection - Machine at 200oC & up to 30 minutes

fig22


Water Absorption

  • Samples constant under water at 40oC
  • Water absoption vs Mechanical properties (120 days)

fig18


UV Radiation

  • Heraeus Suntest CPS at maximum power (756 W/m2)
  • Irradiation vs mechanical properties in time (up to 56 days)

fig19


Coloring

fig21


Recycle Ability

The recycle ability of GG NFR PP is much higher than conventional plastics. 100% scrap of GG NFR PP can be recycled 7 times with maximum 11% downgrade. Please click here for further information.