Properties of GG NFRPP PDF Print E-mail

Property Table of GGF022J *


Properties
性能
Test Method
方法
Test Condition
条件
GGF022J Unit
单位
Melt Flow Rate
熔体质量流动速率
ISO 1133/ASTM
D1238/GB3682-83
200°C, 10 kg 6 g/10min
230°C, 2.16 kg 1
Density
密度
ISO 1183/ASTM
D792/GB3682-83
1.33 g/cm3
Tensile Strength
拉伸强度
ISO 527/ASTM
D638/GB1040-79
23°C, 50% 56 MPa
Tensile Modulus
拉伸模量
5,100
Tensile Elongation
拉伸长度
2.9 %
Flexural Strength
弯曲强度
ISO 178/ASTM
D790/GB9341-88
23°C, 50% 81 MPa
Flexural Modulus
弯曲模量
4,600
Flexural Elongation
弯曲延伸率
3.6 %
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 23°C, 50% 22 kJ/m2
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 3.5 kJ/m2
Heat Deflection Temperature
热变形温度
ISO 75 /
ASTM D648
0.45 MPa 151 °C
1.82 MPa 129
Shrinkage
收缩率
0.2 – 0.5 %
Flammability UL94
阻燃性
IEC60695-11-10 4mm 5VB
2.5mm V0
1.5mm

V0


Property Table of GGN023J *

Properties
性能
Test Method
方法
Test Condition
条件
GGF022J Unit
单位
Melt Flow Rate
熔体质量流动速率
ISO 1133/ASTM
D1238/GB3682-83
200°C, 10 kg 7
g/10min
230°C, 2.16 kg 2
Density
密度
ISO 1183/ASTM
D792/GB3682-83

1.04 g/cm3
Tensile Strength
拉伸强度
ISO 527/ASTM
D638/GB1040-79
23°C, 50% 56
MPa
Tensile Modulus
拉伸模量
4,100
Tensile Elongation
拉伸长度
3.8 %
Flexural Strength
弯曲强度
ISO 178/ASTM
D790/GB9341-88
23°C, 50% 79
MPa
Flexural Modulus
弯曲模量
3,300
Flexural Elongation
弯曲延伸率
4.5 %
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 23°C, 50% 22
kJ/m2
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 4
kJ/m2
Heat Deflection Temperature
热变形温度
ISO 75 /
ASTM D648
0.45 MPa 151 °C
1.82 MPa 97
Shrinkage
收缩率


0.2 – 0.5 %

Property Table of GGN026J *

Properties
性能
Test Method
方法
Test Condition
条件
GGF022J Unit
单位
Melt Flow Rate
熔体质量流动速率
ISO 1133/ASTM
D1238/GB3682-83
200°C, 10 kg 5
g/10min
230°C, 2.16 kg 1
Density
密度
ISO 1183/ASTM
D792/GB3682-83

1.11 g/cm3
Tensile Strength
拉伸强度
ISO 527/ASTM
D638/GB1040-79
23°C, 50% 62
MPa
Tensile Modulus
拉伸模量
5,400
Tensile Elongation
拉伸长度
2.3 %
Flexural Strength
弯曲强度
ISO 178/ASTM
D790/GB9341-88
23°C, 50% 89
MPa
Flexural Modulus
弯曲模量
4,900
Flexural Elongation
弯曲延伸率
2.9 %
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 23°C, 50% 2122
kJ/m2
Charpy impact, notched
缺口冲击强度
ISO 179 – 1 / 1eA 4
kJ/m2
Heat Deflection Temperature
热变形温度
ISO 75 /
ASTM D648
0.45 MPa 156 °C
1.82 MPa 134
Shrinkage
收缩率


0.2 – 0.5 %

* The above values are obtained by testing under standard room temperature. These values are only for reference and not definitive. Changes in working condition may result in end product characteristics which may deviate from above.


OTHER PROPERTIES of GG NFR PP

fig15

 

  Flame Test

  •    Test according to UL94
  •    GG NF50PP: 50% Nature Fiber (Flex)
  •    Flame Retardant: Halogen, aluminum, Magnesium free
  •   


Rheology: Rosand Capillary Rheometer

fig28


Machine Residence Time: Hot Melting Injection - Machine at 200oC & up to 30 minutes

fig22


Water Absorption

  • Samples constant under water at 40oC
  • Water absoption vs Mechanical properties (120 days)

fig18


UV Radiation

  • Heraeus Suntest CPS at maximum power (756 W/m2)
  • Irradiation vs mechanical properties in time (up to 56 days)

fig19


Coloring

fig21


Recycle Ability

The recycle ability of GG NFR PP is much higher than conventional plastics. 100% scrap of GG NFR PP can be recycled 7 times with maximum 11% downgrade. Please click here for further information.


 

 

 

Contact Us

Feel free to get in touch with us!

Address:
Rm. 702, 7/Fl.,
Nan On Comm. Building,
69A Wuhu Street,
Hung Hom, Kowloon,
HKSAR
Tel: +852-24932283
Email: shinebase@ecoplastic.com.hk 


Profile Information

Application afterLoad: 0.000 seconds, 0.29 MB
Application afterInitialise: 0.014 seconds, 0.95 MB
Application afterRoute: 0.019 seconds, 1.42 MB
Application afterDispatch: 0.032 seconds, 2.19 MB
Application afterRender: 0.044 seconds, 2.46 MB

Memory Usage

2593824

11 queries logged

  1. SELECT *
      FROM jos_session
      WHERE session_id = '4us379gjbrd45b4lc14snftn71'
  2. DELETE
      FROM jos_session
      WHERE ( time < '1669768820' )
  3. SELECT *
      FROM jos_session
      WHERE session_id = '4us379gjbrd45b4lc14snftn71'
  4. INSERT INTO `jos_session` ( `session_id`,`time`,`username`,`gid`,`guest`,`client_id` )
      VALUES ( '4us379gjbrd45b4lc14snftn71','1669769720','','0','1','0' )
  5. SELECT *
      FROM jos_components
      WHERE parent = 0
  6. SELECT folder AS type, element AS name, params
      FROM jos_plugins
      WHERE published >= 1
      AND access <= 0
      ORDER BY ordering
  7. SELECT m.*, c.`option` AS component
      FROM jos_menu AS m
      LEFT JOIN jos_components AS c
      ON m.componentid = c.id
      WHERE m.published = 1
      ORDER BY m.sublevel, m.parent, m.ordering
  8. SELECT template
      FROM jos_templates_menu
      WHERE client_id = 0
      AND (menuid = 0 OR menuid = 125)
      ORDER BY menuid DESC
      LIMIT 0, 1
  9. SELECT a.*, u.name AS author, u.usertype, cc.title AS category, s.title AS section, CASE WHEN CHAR_LENGTH(a.alias) THEN CONCAT_WS(":", a.id, a.alias) ELSE a.id END AS slug, CASE WHEN CHAR_LENGTH(cc.alias) THEN CONCAT_WS(":", cc.id, cc.alias) ELSE cc.id END AS catslug, g.name AS groups, s.published AS sec_pub, cc.published AS cat_pub, s.access AS sec_access, cc.access AS cat_access 
      FROM jos_content AS a
      LEFT JOIN jos_categories AS cc
      ON cc.id = a.catid
      LEFT JOIN jos_sections AS s
      ON s.id = cc.section
      AND s.scope = "content"
      LEFT JOIN jos_users AS u
      ON u.id = a.created_by
      LEFT JOIN jos_groups AS g
      ON a.access = g.id
      WHERE a.id = 82
      AND (  ( a.created_by = 0 )    OR  ( a.state = 1
      AND ( a.publish_up = '0000-00-00 00:00:00' OR a.publish_up <= '2022-11-30 00:55:20' )
      AND ( a.publish_down = '0000-00-00 00:00:00' OR a.publish_down >= '2022-11-30 00:55:20' )   )    OR  ( a.state = -1 )  )
  10. UPDATE jos_content
      SET hits = ( hits + 1 )
      WHERE id='82'
  11. SELECT id, title, module, position, content, showtitle, control, params
      FROM jos_modules AS m
      LEFT JOIN jos_modules_menu AS mm
      ON mm.moduleid = m.id
      WHERE m.published = 1
      AND m.access <= 0
      AND m.client_id = 0
      AND ( mm.menuid = 125 OR mm.menuid = 0 )
      ORDER BY position, ordering

Language Files Loaded

Untranslated Strings Diagnostic

None

Untranslated Strings Designer

None